刘庆
,
刘振纲
,
姚枚
金属学报
研究了温轧态Al-Li-Cu-Mg-Zr合金经不同拉伸条件超塑变形后残余强度及其与空洞行为的关系结果表明在一定应变量范围内,以高的应变速率变形的试样比以低的应变速率变形的试样空洞少,残余强度高;在变形到较大的应变量时,先快后慢的两段速率拉伸变形与一段速率拉伸相比,试样中空洞少,残余强度高结合该合金变形初期发生的形变促使连续再结晶过程,讨论了拉伸条件与空洞行为及残余强度的关系
关键词:
Al-Li-Cu—Mg—Zr合金
,
superplastic deformation
,
residual strength
,
cavitation
CUI Jianzhong MA Longxiang Northeast University of Technology
,
Shenyang
,
China Department of Metals Forming
,
Northeast University of Technology
,
Shenyang
,
China
金属学报(英文版)
The method controlling grain shape in TMT processing and the effect of grain shape on char- acteristic parameters in superplastic deformation were discussed.The accommodation velocity of grahl boundary sliding,which is the dominant mechanism in superplastic deformation,and the contribution of each mechanism to the total strain,as influenced by grain shape,were ana- lyzed.Grain shape has been shown to be an essential structural factor for superplasticity.Then an analysis was made about the effect of grain shape on the region transition strain rate so that a new concept,critical aspect for superplasticity,was worked out.These predictions were compared with the measured results in an Al-Zn-Mg alloy.
关键词:
superplastic deformation
,
null
,
null
,
null
,
null
王春荣
,
朱桂秋
,
刘兴志
材料研究学报
用S_4—10型扫描电镜,对Sn-3.36wt-%Bi 超塑合金以ε=1×10~(-3)min~(-1)作单轴拉伸的动态观察,发现晶粒形貌发生了明显的变化,晶粒成晶团产生了转动,部分垂直或近似垂直于外力的晶界被宽化,出现晶粒湮没、置位、分解和结合过程。在试样形变过程中,没有发现晶粒长大现象,而是聚合成晶团后运动。
关键词:
动态观察
,
grain morphology
,
superplastic deformation
JIANG Xinggang CUI Jianzhong MA Longxiang Northeast University of Technology
,
Shenyang
,
China
金属学报(英文版)
The fractal dimension changes of cavities have been determined during superplastic deformation of the high strength aluminiurn alloy 7475 with different strain,temperature, strain rate and grain size.The fractal dimension of cavities may increase with the increase of strain.It becomes higher as the alloy deformed under lower temperatures,greater strain rate and coarser grain size.The alloy would be approaching to rupture if the fractal dimension of cavities raised to a certain extent.
关键词:
fractal dimension
,
null
,
null
,
null
郑漫庆
,
王高潮
,
喻淼真
,
徐雪峰
材料工程
doi:10.11868/j.issn.1001-4381.2014.08.006
采用应变速率循环法在超塑拉伸机上对TC4-DT钛合金进行三组高温超塑性拉伸实验,变形温度为850～890℃,应变速率为3.3×10-5～3.3×10-3s-1.通过对拉伸实验数据的分析计算出TC4-DT钛合金动态再结晶激活能,并利用Arrhenius模型构建TC4-DT高温条件下的超塑性本构方程.结果表明:TC4-DT钛合金的流动应力对变形温度较为敏感,随着温度的升高,流变应力逐渐减小,软化机制愈发明显,870℃附近的超塑性较好,伸长率达到554％.
关键词:
TC4-DT
,
应变速率循环
,
本构方程
,
超塑性变形
董洪波
,
王高潮
,
曹春晓
材料热处理学报
为了研究TC11(Ti-6.5Al-3.5Mo-1.5Zr-0.3Si)钛合金的超塑性变形行为,采用两种改锻工艺细化坯料原始组织,然后在电子拉伸试验机上分别以恒速、恒应变速率和最大m值法进行拉伸实验.结果表明,TC11钛合金在α+β区通过三维镦拔改锻工艺,可以获得晶粒度为6μm的细晶等轴组织,而在β区拔长改锻的组织为粗大的魏氏组织.在变形温度为900℃的条件下,TC11钛合金通过最大m值超塑变形方式获得了异常高的超塑性,最大伸长率达到2300%;而采用常规的恒应变速率和恒速超塑变形,伸长率分别为1147%和1100%.说明TC11钛合金在α+β区通过三维镦拔改锻细化晶粒后,以最大m值超塑变形是获得较好超塑性的有效方法.
关键词:
TC11钛合金
,
超塑性
,
最大m值超塑变形
,
变形工艺
李理
,
张新明
,
邓运来
,
周楠
,
唐昌平
中国有色金属学报
采用电子显微镜和XRD研究分析Mg-Gd-Y-Zr合金挤压棒材超塑性拉伸前后的微观组织及其超塑性机制.结果表明:在温度为450 ℃、应变速率为2×10~(-4) s~(-1)的变形条件下获得的挤压棒的最大伸长率为410%,应变速率敏感系数为0.54;合金表观变形激活能远高于镁的晶界扩散激活能或晶格扩散激活能,超塑性变形机制为晶格扩散控制的位错协调晶界滑动机制;微孔洞在基体/方形富稀土相界面处萌生,较软的不规则块状β相承受部分塑性变形,松弛了相界处应力集中.
关键词:
Mg-Gd-Y-Zr合金
,
第二相
,
挤压
,
超塑性变形
谭丽琴
,
王高潮
,
甘雯晴
,
熊城
航空材料学报
doi:10.11868/j.issn.1005-5053.2014.6.002
采用应变速率循环法对TA15钛合金进行三组高温超塑性拉伸试验,变形温度区间为850 ～ 950℃,应变速率循环区间为5×10-6～5×10-4 s-1.分析拉伸试验数据后,计算出TA15钛合金动态再结晶激活能Q,结合金相组织分析得出其热变形过程中发生了动态再结晶的结论;并利用Arrhenius模型构建超塑性本构方程,应用origin数据处理软件进行数据分析,求得TA15钛合金高温条件下的超塑性本构方程.运用1 stopt软件修正了该本构方程,使其精度达到99.3％.结果表明,TA15钛合金的流动应力对变形温度较为敏感,随着温度的升高,流变应力逐渐减小,软化机制愈发明显,且在900℃附近的超塑性较好,伸长率达到了846％.
关键词:
TA15钛合金
,
应变速率循环
,
本构方程
,
超塑性变形